AIMS: Impact of different post-space disinfectants (Saline, Sodium hypochlorite (NaOCl) followed by ethylene-diamine-tetra-acetic acid (EDTA) and curcumin activated by microbubble emulsion (MBE) on the Vickers hardness (VH) of root canal dentin and extrusion bond strength (EBS) of Glass fiber post (GFP) and PEEK post.

Methods: Ninety maxillary central incisors having fully formed roots were included. After the specimen's disinfection, root canal treatment was completed. Post space was prepared by removing gutta-percha using gates glidden drills. Teeth were then arbitrarily allocated into three groups based on the methods of disinfection regime used. Group 1: Saline, Group 2: NaOCl+ EDTA and Group 3: Curcumin activated by MBE (n=30). Analysis of VH of radicular dentin was performed using a micro-Vickers tester on ten samples from each group. After post-space disinfection, twenty specimens from each group were further divided into two subgroups (n=10) In group-1A 2A, and 3A, GFP was used. Whereas, prefabricated PEEK posts were used in 1B, 2B, and 3B subgroups. The PBS and failure modes were performed using a universal testing machine and stereomicroscope respectively. Data was analyzed using ANOVA and Tukey post hoc test to identify significant variations among groups concerning the MH and EBS of the different posts used (p=0.05).

Results: Group 2 (5.25% NaOCl + 17% EDTA) (0.15 ± 0.02 GPa) treated specimens presented lowest scores of VH. However, Group 1 (Saline) irrigated canals displayed the highest scores of surface hardness (0.25± 0.07 GPa). Additionally, a cervical third of 3A (CP activated by MBE + GFP) (11.22±0.79 MPa) presented the highest scores of bond integrity. Whereas Group 1B (Saline + PEEK post) treated specimens presented the lowest scores of PBS (4.15±0.15 MPa).

Conclusion: Curcumin activated by microbubble emulsion for disinfection of canal dentin demonstrated favorable VH. Similarly, glass fiber post-cemented in radicular walls disinfected with curcumin activated with MBE showed promising post-bond integrity to the canal dentin.