Effective Removal of Turquoise Blue Reactive Dyes Using Tubular Furnace Supported Activated Carbon Prepared from Delonix Regia Pods - Kinetics and Thermodynamic Studies
V. Vijayakumar1
, S. Shreedevi1* and Dr.K.Ramesh2
1Department of Chemistry, Arignar Anna Government Arts College, (Affiliated to Thiruvalluvar University), Cheyyar, Tamil Nadu, India.
2Department of Chemistry, Poompuhar College (Autonomous), Melaiyur, Mayiladuthurai DT, Tamilnadu, India.
Corresponding Author E-mail: drssdche2024@gmail.com
Article Publishing History
Article Received on : 01 Jun 2024
Article Accepted on :
Article Published : 09 Jul 2024
This investigation explores “batch adsorption of turquoise blue dye” from aqueous solutions using phosphoric acid-activated “Delonix Regia Pod carbon prepared using a tubular furnace” (DRTFC). Various factors were examined and equilibrium data were gathered at different temperatures (205 K, 315 K, and 325 K) and for varying initial dye concentrations. Optimal pH for dye removal was found to be 2. Kinetic modeling was done using “Lagergren's first-order kinetics”, Ho's “second-order kinetics”, and Weber Morris equations, with the “pseudo-second-order kinetic model” showing the best fit based on Sum of Squared Errors (SSE) analysis. Thermodynamic parameters were determined through “Van’t Hoff plots”, suggesting that the adsorption process was endothermic, spontaneous, and with increased randomness.
KEYWORDS:Adsorption; Delonix Regia Pods; H3PO4; Kinetics; thermodynamics; Turquoise Blue dye
Download this article as:
Copy the following to cite this article:Vijayakumar V, Shreedevi S, Ramesh K. Effective Removal of Turquoise Blue Reactive Dyes Using Tubular Furnace Supported Activated Carbon Prepared from Delonix Regia Pods - Kinetics and Thermodynamic Studies. Orient J Chem 2024;40(4).
Vijayakumar V, Shreedevi S, Ramesh K. Effective Removal of Turquoise Blue Reactive Dyes Using Tubular Furnace Supported Activated Carbon Prepared from Delonix Regia Pods - Kinetics and Thermodynamic Studies. Orient J Chem 2024;40(4). Available from: https://bit.ly/3VZZML9
Introduction
Throughout the dyeing process, over 15% of the world’s total dye production is wasted and emitted as influents 1. One of the most challenging tasks facing the pulp, paper, textile finishing, and dye production industries is the removal of colour from such wastes. Basic dyes are cationic dyes that dissolve in water and are mostly used on acrylic fibres, though they can also be used to colour wool and silk 2. Among all the dyes in its category, turquoise blue dye (IB), a basic dye, is commonly used for “dying cotton, wool, silk, nylon, paper, leather”, etc.
In comparison to every other dye in its class, with very high tinctorial values, basic dyes are the brightest class of soluble dyes; less than 1 milligram per liter of the dye results in a noticeable coloration.
As a result, it is important to remove colours from waste water before discharging into water sources. Waste water can be treated using a variety of techniques to remove dyes. Electrochemical oxidation 3, photodegradation4, electrocoagulation5 and membrane filtration6 and Adsorption7 are a few of them. Adsorption has emerged as the most effective approach among these to treat wastewater. The removal of colours from wastewater has been effectively accomplished using adsorption employing activated carbon as an adsorbent8. A variety of agricultural waste products, such as sawdust, sunflower seeds, tamarind fruit shells, coir pith, and cashew nut shells, are utilized as precursors to prepare activated carbon.
This study investigates the viability and effectiveness of using Delonix Regia Pods in adsorption methods to extract the cationic dye Turquoise Blue dye (TB) from artificial aqueous solutions. To learn more about the adsorption properties of Delonix Regia Pods, researchers looked at the impacts of temperature, adsorbent dose, adsorbate concentrations, and contact time.
Symbols and Subscripts
Symbols and Subscripts
Ci , Ct and Ce
“Initial Conc. of TB dye soln., at the time ‘t’ and at equilibrium respectively”
qe & qt
“Quantity adsorbed at the equilibrium ‘t’ at time respectively”
‘V’
“Volume of the TB dye soln in liter (L)”
‘W’
“Mass of a carbon” in (g)
‘R’
“Gas Constant”
‘T’
“Temperature” (K)
‘k1’
“First-Order rate constant” of adsorption (l/Min)
‘k2’
“Second-order rate constant”
‘T’
“Time in minutes”
‘h’
“Initial adsorption rate” (milligram per liter min)
‘kp’
“Intra-particle diffusion rate constant”
‘C’
“Thickness of the boundary film”
‘N’
“No. of data points”
‘Kc’
“Equilibrium constant”
‘∆G°’
“Standard free energy”
‘∆S°’
“Entropy of adsorption”
‘∆H°’
“Enthalpy of adsorption”
Tools for Processing Data
Tools for Processing Data
S. No.
Framework
Formulae
1.
Mass balance relationships
% of Removal
“(Ci – Ct)×V/Ci
Quantity adsorb. at equilibrium, qe
(Ci – Ce) ×V/W
Quantity adsorb. at the time t, qt
(Ci – Ct) × V/ W”
2.
Kinetic Models & SSE %
Pseudo First order kinetics [9]
(Legergren equation)
“log (qe-qt)=log qe – k1 /2.303 × t
Pseudo Second order kinetics [10]
(Ho equation)
The initial adsorp. rate is h
t/qt=1/ k2.qe2 +1/qe t
h = k2qe2
Intra particle diffusion [11]
(Weber–Morris equation)
qt = kpt1/2 + C
Sum of error square
SSE (%) = √∑[(qe)exp-(qe)cal]2/ N”
3.
Thermodynamic Parameters
Standard Free energy Change
∆G° =-RT ln Kc
“Van’t Hoff equation” [12]
ln Kc =∆S°/R – ∆H°/RT
Materials and Methods
Composition of adsorbate
The dye stock solution was made using Analar grade turquoise blue dye, which was dissolved to concentration of 1000 milligram per liter in double-distilled water using an appropriate amount of precisely weighed dye. By carefully diluting the stock solution, the experimental solutions were created.
Preparation of Adsorbent
To get rid of any surface dust, distilled water was used to wash the delonix regia leaves. After that, they were sun-dried, cut into tiny pieces, and processed with a pulverizer into a powder. One hundred millilitres of a 60% H3PO4 solution and fifty grammes of pod powder were mixed together and allowed to sit at room temp. for a full day. After that, the materials were heated for two hours at 800 oC in a nitrogen environment at a rate of 1°C per minute. After that, the carbon sample were cleaned with 0.5 M HCl and deionized water until the washing liquid’s pH reached 7.0, which is neutral. After that, the material was dried for an hour at 383 K in a hot oven. Ultimately, the dehydrated material was crushed and filtered to produce particles with an average size between 150 and 300 µm. Delonix Regia Pod Activated Carbon is the name given to this processed material (DRTFC).
Batch adsorption experiments
The “adsorption of turquoise blue dye on DRTFC” investigated by manipulation of multiple process factors, like ‘temperature’, ‘adsorbent ratio’, ‘contact time’, and ‘initial dye concentration’. A predetermined amount of DRTFC was added 50 millilitres of the “dye solution”. A mechanical shaker running at 180 rpm was used to fully agitate the mixture for the predetermined amount of time. The solution was then centrifuged, and using a ‘Systronics 2202 UV-Visible spectrophotometer’, the remaining colour in the centrifuged solution was measured spectrophotometrically at a wavelength of 780 nm.
“Kinetic models” were applied and experimental data about the initial dye concentration and contact time were used for assessment.
Results and Discusion
Effect of adsorbent dosage
Adsorbent dosages of 5, 10, 20, 30, 40, 50, 60, 70, 80, 90, and 100 Mg were added to 50 ML of “dye solution” at a 50 milligram per liter concentration to conduct the investigation. Fig. 1 illustrates how the percentage of dye removed from an aqueous solution rises as the carbon dose raises. This is because there are more adsorption sites and a larger surface area of carbon [13, 14]. The homogeneous adsorbing sites are indicated by the smooth curve. These findings led to the adsorbent dose of 40 mg/50 mL being used for the following experiments, which gave a removal percentage of 71.02%.
Impact of duration of contact
The starting concentrations for this investigation were 25, 50, and 75 mg/L solutions. The findings are displayed in Fig. 2. At first, the proportion of dye removed increases quickly as contact duration increases; after that, it increases gradually, and after 100–180 minutes, no discernible change is seen. It was discovered that when the original concentration of dye solution increased, the percentage of dye dropped.
Adsorption dynamics
Kinetic studies are needed to define reaction mechanism of adsorption process. Different kinetic models like “pseudo-first-order, pseudo-second-order, and intra-particle diffusion kinetic models” were analyzed in the adsorption of TB dye onto DRTFC.
Pseudo first–order kinetic model
Table 1: Pseudo first order Kinetics results for TB dye onto DRTFC
“Pseudo First Order Kinetics”
Initial
Conc.
Ci (Mg/L)
k1
(min–1)
qe, cal (mg g-1)
qe, exp (mg g-1)
∆qe
R2
MSSE
25
0.0339
12.3537
20.74
-8.38
0.8776
3.97
50
0.0320
25.5035
35.4
-9.89
0.9692
75
0.0272
33.9938
48.38
-14.38
0.9631
[PH = 2; Dose = 40 Milligram per liter 50 Milli Liter; Agitation time = 180 min; Temp=305K]
Pseudo–second order kinetic model:
The data obtained for “adsorption kinetics” was further analyzed employing “pseudo first order” and the “pseudo second order models”. Additionally, the initial concentrations of adsorbate had a substantial positive correlation with the first phase of adsorption. The results for the ‘R2 values’ for the “pseudo-first-order” model were between 0. 995 and 0. 997, and for ‘R2 values’ for the “pseudo-second-order model” were between 0. 998 and 0. 999. In order to choose the most suitable model the theoretical uptake (qe(cal)) obtained from the models was compared with the experimental qe (qe(exp)). The model that has the greatest number of elements with approximate qe(cal) values to the qe(exp) values is said to be the best fit model. This is measured by the Mean Sum of Squared Error (MSSE), and smaller values are more desirable, suggesting a more accurate model. The “pseudo-second-order model” yielded lowest MSSE and hence, most appropriately described the adsorption data, thereby underlining that it was the most suitable model for describing the adsorption kinetics. The low diff. between qe(cal) and qe(exp) as compared to the “pseudo-first-order kinetic model” defines that the present model is better.
Table 2: Pseudo second order Kinetics results for TB dye onto DRTFC
Pseudo Second Order Kinetics
Initial
Concentration
Ci (mg/L)
k2
(g mg-1 min-1)
qe, cal
(mg g-1)
qe(exp)(mg/g)
∆qe
‘h’
(mg/g min)
R2
MSSE
25
0.0092
21.3675
20.74
0.6275
4.2088
0.9984
0.74
50
0.0035
37.0370
35.4
1.6370
4.7348
0.996
75
0.0022
50.5050
48.38
2.1251
5.7013
0.9949
Intraparticle diffusion model
In the prior research it has been proved that the adsorption process is a multistep event here the molecules of solute are transferred from the fluid phase to the surface of adsorbent and then to the inside of the pores and this stage is usually slow [15-18]. The multilinearity of the qt versus t1/2 plots also supports the population of these phases in the adsorption mechanism. As revealed by the slope and intercept values separately estimated in this study (Table 3), the kp and C values suggest that the adsorption rate constants are higher at higher initial dye concents. This indicates that a significant factor influencing the total rate of the “adsorption process” is the rate of dye diffusion within the sorbent particles’ pores.
Table 3: Intra Particle Diffusion results for TB dye on to DRTFC
Initial Concen.
Ci (milligram per liter)
Intra Particle Diff.
C (mg g-1)
kp (mg g-1 min-1)
R2
25
10.269
1.1239
0.9976
50
11.943
2.4158
0.9943
75
20.214
2.5959
0.9986
[PH = 2; Dose = 40 Milligram per liter 50 milliliter; Agitation time = 180 min; Temp=305K]
Adsorption thermodynamics
The “Van’t Hoff” plots demonstrate a high linearity of ln Kd against 1/T. The ΔG° values are obtained utilizing the Kd and T data analysis. From the plots of log [K] against 1/T. The “enthalpy (ΔH°) & entropy (ΔS°)” changes are calculated by the intercepts and slopes respectively as shown in the Table 4 and Fig. 6.
In all the tested systems, the ΔG° values are negative, which support the occurrence of the favorable and spontaneous adsorption processes. The positive ΔH° values imply the endothermic process and values of 1–93 kJ mol¯¹ support the view that physisorption is the main mechanism (Author, Year). Positive ΔS° values signify an increase in unpredictability, particularly near the interface between the “solid-solution.” Because adsorbate species use a portion of translational entropy, their displacement of water molecules is likewise linked to increased randomness[19-21]. Higher temperatures may increase the size of pores and stimulate activity on the adsorbent surface and improve its adsorption ability.
Table 4: Thermodynamic parameters of TB dye by Delonix Regia Pods
Ci(mg/L)
ΔG (kJ mol-1)
ΔH (kJ mol-1)
ΔS (Jk-1 mol-1)
303 K.
313 K.
323 K.
25
-3.6674
-4.1430
-4.6646
-11.532
49.8092
50
-2.4983
-3.1532
-3.4117
-11.49
46.0845
75
-1.9029
-2.1372
-2.7570
-11.049
42.2933
Conclusion
In a recent study, the feasibility of using carbon activated with phosphoric acid derived from pods of Delonix Regia was investigated for the removal of a “turquoise blue dye” from water. In batch adsorption studies, it was observed that the activated carbon could remove the dye efficiently to a significant amount. The equilibrium was attained in 100-180 minutes using 40mg of adsorbent for every 50mL of solution at 305K. The optimum pH for adsorption was 2 for initial dye concentrations of 25-75mg/L. The results of the kinetics analysis showed that the “pseudo second-order kinetics” best described the adsorption process and “intraparticle diffusion” was the major role play in the mechanism. “Thermodynamic studies” suggested that the adsorption process was spontaneously endothermic with increased randomness.
Acknowledgement
The author would like to acknowledge the faculty of Arignar Anna Government Arts College, (Affiliated to Thiruvalluvar University), Cheyyar, Tamilnadu.
Conflict of Interest
The author declares no conflict of interest
References
Rania Al-Tohamy.; Sameh S. Ali.; Fanghua Li .; Kamal M. Okasha .; Yehia, A.; Mahmoud, G.; Tamer Elsamahy.; Haixin Jiao .; Yinyi Fu .; Jianzhong Sun. Ecotoxicology and Environmental Safety. 2022, 231, 113160.
This work is licensed under a Creative Commons Attribution 4.0 International License.