Bamboo derived activated carbon as highly efficient catalysts for the oxidation and adsorption of hydrogen sulfide at room temperature

A series of bamboo derived activated carbon (BAC) with different activation degree were prepared and tested for H2S catalytic oxidation-adsorption at room temperature. It was found that the specific surface area, pore size and defect level increased with the increase in activation degree. The highest sulfur capacity (Qs)can be obtained for Na/BAC-8, which can attach 0.73g/g. And the Qs was directly related to the total pore volume and specific surface area. Meanwhile, the final sulfate and elemental sulfur products were mainly formed in small micropores (<0.7nm) and mesopore, respectively. The competitive adsorption of excess water with H2S did not occur even under high RH condition due to the highly hydrophobic nature and the partial consumption of water. Moreover, the diffusion process and adsorption kinetics of the sulfur containing products were explored for the first time. Diffusion in the pores rather than between the pores was the rate-determining step during the diffusion process of sulfur-containing products. The adsorption kinetics are dominated by internal diffusion. The reaction mechanism was investigated by using in situ DR-FTIR and DFT methods. SO3 was the important intermediate species during the reaction. And the polymerization of sulfur atom to form stable S8 cluster and the formation of SO2 were the rate determining step for the generation of elemental sulfur and sulfate, respectively.

You have access to this article

Please wait while we load your content... Something went wrong. Try again?

留言 (0)

沒有登入
gif