Available online 21 January 2023
Author links open overlay panelHighlights•The investigation surveyed modified adhesives containing 45S5 bioglass with calcium fully replaced by strontium.
•The role of bioglass silanization was also investigated in terms of dentin bonding and remineralization.
•In general, bioglass containing strontium did not achieve better outcomes than calcium-based fillers.
•The silanization of traditional 45S5 bioglass improved dentin remineralization and increased bond strength after aging.
•Simplified adhesives with 45S5 bioactive glass are promising remineralization agente triggering therapeutic effects.
AbstractObjectiveTo analyze simplified adhesive containing pure or silanized bioglass 45S5 (with calcium) or Sr-45S5 (strontium-substituted) fillers applied on dentin and to evaluate the microtensile bond strength (µTBS), interface nanoleakage, degree of conversion of adhesive, collagen degradation and remineralization.
MethodsAmbar Universal adhesive (FGM) was doped with 10 wt% bioactive glasses to form following groups: Control (no bioglass), 45S5 (conventional bioglass 45S5), Sr-45S5 (Sr-substituted bioglass 45S5), Sil-45S5 (silanized bioglass 45S5) and Sil-Sr-45S5 (silanized bioglass Sr-45S5). Adhesives were applied after dentin acid-etching using phosphoric acid at extracted human molars. Resin-dentin sticks were obtained and tested for µTBS, nanoleakage at 24 h or 6 months. Degree of conversion was measured using micro-Raman spectroscopy. Dentin remineralization was assessed by FTIR after 6-month storage in PBS. Hydroxyproline (HYP) release was surveyed by UV-Vis spectroscopy. Statistical analysis was performed using ANOVA and Tukey’s test (p < 0.05).
ResultsRegarding µTBS, Sr-45S5 and 45S5 presented higher and stable results (p > 0.05). Control (p = 0.018) and Sil-Sr-45S5 (p < 0.001) showed µTBS reduction after 6-month aging. Sil-Sr-45S5 showed higher HYP release than that obtained in the 45S5 group. Sil-45S5 showed mineral deposition and increase in µTBS (p = 0.028) after 6-months. All experimental adhesives exhibited higher degree of conversion compared to Control group, except for 45S5. All adhesives created gap-free interfaces, with very low silver impregnation, except for Sil-Sr-45S5.
SignificanceThe incorporation of silanized 45S5 bioglass into the universal adhesive was advantageous in terms of dentin remineralization, bonding performance and adhesive polymerization. Conversely, Sil-Sr-45S5 compromised the µTBS, interface nanoleakage and had a negative impact on HYP outcomes.
KeywordsDentin
Remineralization
Bioglass
Strontium
Silanization
View full text© 2023 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.