Crystallinity and flame retardancy are two key properties for poly(lactic acid)(PLA) in applications. In this paper, a quaternary phosphonium salt poly(ionic liquid) (PIL) and a phosphamide (POFA) were prepared. The PIL, POFA and their blend were used to regulate the flame retardancy and crystallization behaviors of PLA using the limiting oxygen index, UL-94 vertical burning, and thermogravimetric analysis, and differential scanning calorimetry etc. The results showed that a synergistic effect exists between PIL and POFA on flame retardancy. When 6 wt% PIL/POFA (2/1) was added into PLA, its LOI value is 28.0 vol%, and achieves the UL-94 V-0 rating while the PLA composites containing 6 wt% PIL or POFA just achieve the UL-94 V2. The PIL/POFA improves the flame retardancy of PLA by melting-away mode. In addition, the crystallization rate of PLA containing PIL/POFA is faster than that of PLA/PIL and PLA/POFA. The degradation of PLA induced by PIL/POFA produces some small molecular oligomers, which enhances the molecular chain mobility and rearrangement, thus contributes to better flame retardancy and faster crystallization.